ALUMINIUM INGOTS
Chemical Composition: Al
Weight: 20/25kg
Al (Min): 99.7%-99.9%
Place of Origin: China
Appearance: silvery white
Aluminum ingot for remelting is produced by molten salt electrolysis method using alumina and cryolite. Products meet the national standard GB/T1196-2002. The surface of ingot is clean and smooth.
Applications:
1. mainly used for melting ingot
2. discontinuous melting with scrap
3. easy control and operation
4. fast melting
5. Used for industry such as automobile,pinning and weaving,electron broadly and so on
The main models are as follows: AL99.90, AL99.85, AL99.70A, AL99.70, AL99.60, AL99.50, AL99.00
Product Description
Description
Product Description
Chemical Composition: Al
Weight: 20/25kg
Al (Min): 99.7%-99.9%
Place of Origin: China
Appearance: silvery white
Aluminum ingot for remelting is produced by the molten salt electrolysis method using alumina and cryolite. Products meet the national standard GB/T1196-2002. The surface of the ingot is clean and smooth.
Applications:
1. mainly used for melting ingot
2. discontinuous melting with scrap
3. easy control and operation
4. fast melting
5. Used for industry such as automobile,pinning and weaving,electron broadly and so on
The main models are as follows: AL99.90, AL99.85, AL99.70A, AL99.70, AL99.60, AL99.50, AL99.00
| Grade | Chemical Composition % | |||||||||
| Al≥ | impurities ≤ | |||||||||
| Si | Fe | Cu | Ga | Mg | Zn | Mn | others | Sum | ||
| Al99.9 | 99.90 | 0.50 | 0.07 | 0.005 | 0.02 | 0.01 | 0.025 | – | 0.010 | 0.10 |
| Al99.85 | 99.85 | 0.80 | 0.12 | 0.005 | 0.03 | 0.02 | 0.030 | – | 0.015 | 0.15 |
| Al99.7 | 99.70 | 0.10 | 0.20 | 0.010 | 0.03 | 0.02 | 0.030 | – | 0.030 | 0.30 |
| Al99.6 | 99.60 | 0.16 | 0.25 | 0.010 | 0.03 | 0.03 | 0.030 | – | 0.030 | 0.40 |
| Al99.5 | 99.50 | 0.22 | 0.30 | 0.020 | 0.03 | 0.05 | 0.050 | – | 0.030 | 0.50 |
| Al99.00 | 99.00 | 0.42 | 0.50 | 0.020 | 0.03 | 0.05 | 0.050 | – | 0.050 | 1.00 |